ALL CATEGORIES

Seller Center
- Product Management
  
  Post Product
  
  Manage Products
  
  Featured Products
- Blog Management
  
  Post Blog Article
  
  Manage Blog Articles
  
  Manage Blog Categories
- Inquiry Management
  
  My Inquiries
  
  Buying Requests
- Analytics Center
  
  Performance Dashboard
  
  Product Analytics
  
  Visitor Analytics
Connect Your Store to WeChat

Follow Our Official Service Account
Manage Products & Inquiries Anywhere
Seller Services

Seller Services

SupplierGO.com: 20 years of Global Trade Expertise, Empowering Your Business to Go Global!

Join SupplierGO.com

Free & Instant Registration

Showcase Company & Products

Access Global Buying Requests

Register Now

Activate Verified Supplier Membership

Priority Verified Visibility

Claim Exclusive Buying Requests

Automated Multi-language Store

Verified Now

Launch Your EasyOcean Website

Full-Service Website Management

Google Page 1 Guarantee

Enhanced Brand Credibility

Launch Now
Buyer Services
Post Buying Request

Browse Product Categories

Featured Suppliers
Contact Platform Support

Help Center

Home > Metallurgy, Mineral & Energy > Steel & Products > Steel Sheet & Plate > Hot Work Tool Steel H13/1.2344/SKD61plate Plastic Sheet Pile

Hot Work Tool Steel H13/1.2344/SKD61plate Plastic Sheet Pile

US$ 2,245 - 2,470 MOQ: 1 Ton

Key Specifications

Get Latest Price

Standard:

AISI, ASTM, BS, DIN, GB, JIS, AISI, ASTM, GB, JIS, DIN, BS

Grade:

H13

Thickness:

16mm-500mm

Contact Supplier Request Quote Chat Now

Dongguan City Yaoteng Special Steel Co., Ltd.

Payment & Shipping

Payment Methods:

Port of Shipment:

shenzhen or guangzhou port

Delivery Detail:

Delivery time depends on order quantity.

Product Details
Company Profile
Contact Us

Standard AISI, ASTM, BS, DIN, GB, JIS, AISI, ASTM, GB, JIS, DIN, BS

Grade H13

Thickness 16mm-500mm

Place of Origin Shandong, China

Brand Name OT

Model Number H13

Type Steel Plate

Technique Hot Rolled

Surface Treatment Coated

Application Other, Container Plate, Structural Steel Bar, Tool Steel Bar, Die Steel Bar

Special Use High-strength Steel Plate

Width 105mm-1500mm

Length 2000mm-5800mm or as customers request

Hot Work Tool Steel SKD61, Forged SKD61 Steel, Turned Surface SKD61 Tool Steel

1.ChemicalComposition(%)

C	Si	Mn	P	S	Cr	Mo	V
0.32-0.45	0.80-1.20	0.20-0.50	≤ 0.03	≤ 0.03	4.75-5.50	1.10-1.75	0.80-1.20

2.Equivalent Grades

X40CrMoV5,1.2344,SKD61,H13

3.Form&Size

1)SKD61 Tool Steel round bars, flat/square bars,plates,sheets.

2)SKD61 Tool Steel Size Available(Length can be customized)

4.Round bar

Round steel bar 10-800mm

5.Flat bar

Flat steel bar 6-400mm*200-1600mm

6.Surface Condition

H13(1.2344/SKD61), EFS H13(8407), 1.2714(SKT4/5CrNiMoV)

7. Characteristic

pure steel vacuum degassing refining process ball the annealing softening treatment, good cutting performance. SKD61 picture strengthening elements vanadium, molybdenum special Add, abrasion resistance is extremely excellent

8. Usage

SKD61 a high-carbon high-chromium alloy tool steel with high hardness and wear resistance after heat treatment and hardenability, good dimensional stability, suitable for making high-precision long-life cold work die and thermosetting molding plastic mold.

9. Physical properties

SKD61 Hardness: before heat treatment SKD61 about HRC15 ~ 20 (HB200 230), the hardness after heat treatment: the internal of HRC40 ° ~~ 45 ° surface HV1000 ± 100 SKD61 density is 7.85 g per cubic centimeter

10.heat treatment

Quenching: the first stage of warm-up: the second stage of 500 to 550 ° C Preheat: 750 ~ 800 °C quenching or high-pressure gas cooling, 100 ~ 150 °C into the back to the stove. Tempering: Preheat: 300 to 350 °C tempering heating: 550 to 680 °C air cooling to room temperature, tempering three times. Quenching temperature of 1020 to 1050 degrees, hardness 56 ~ 58HRC, heat treatment of small deformation, surface nitriding nitriding processing products have better wear resistance.

11. Cryogenic treatment

In order to obtain the highest hardness and dimensional stability, the mold immediately after the quenching cryogenic -70 to -80 ° C., maintained for 3-4 hours, and then in the tempering treatment, the cryogenic treatment of tool or mold hardness than the hardness of conventional heat treatment 1 -3HRC. Complex shape and size changes in large parts, cryogenic processing production risk of cracking