Contact Platform Support
Help CenterExcellent Carbon Brick 89% for Furnace Lining, Taphole
Related Products
-
Carbon Brick for Hot Metal Ladle and Steel LadleUS$ 3 - 5MOQ: 10 Pieces -
EAF, Ladles and Steel Ladle Conductivity Refractory Carbon BricksUS$ 3 - 5MOQ: 10 Pieces
-
Industrial Furnace Lining Used Resin Bond Magnesia Carbon BrickUS$ 3 - 5MOQ: 10 Pieces
-
Favorites Compare Resin Bonding Magnesia Carbon Brick for Steel IndustryUS$ 3 - 5MOQ: 10 Pieces
-
For Steel Ladle Furnaces Magnesia Carbon Refractory BrickUS$ 3 - 5MOQ: 10 Pieces
Specifications
1. good resistance to high-temperature2. oxidation&slag erosion
3. long working life and high bulk
4. high refractability
JX GRAPHITE BRICK AND CARBON BRICK
The JX graphite brick and carbon brick are widely used as the lining material in various of high temperature furnace or chemical equipment. In many chemical processes, the equipment and reaction vessels must be protected against the acidic and caustic materials used in the processes. The linings made from ceramic or synthetic plastic type materials are often unsuitable, since they may not withstand chemical attack, high temperature or sudden temperature changes. Alkaline solutions and hydrofluoric acid are of great importance in chemical technology, but they rapidly destroy equipment linings not made of carbon containing materials.
TECHNICAL PROPERTY FOR GRAPHITE BRICK
Test Item |
unit |
JX- GZ1 |
JX- GZ2 |
JX- GZ3 |
Electric Resistance |
μ Ωm |
8.3 |
≤8. |
≤9.0 |
Bulk Density |
g/cm³ |
1.72-1.74 |
1.70-1.72 |
1.68-1.70 |
Grain Size |
mm |
0.8 |
0.8 |
0.8 |
Compressive Strength |
M pa |
40 |
≥35 |
≥32 |
Bending Strength |
M pa |
17.5 |
≥14.5 |
≥14.5 |
Porosity |
% |
18 |
≤20 |
≤22 |
Ash Content |
% |
0.09 |
≤0.2 |
≤0.3 |
C.T.E.( to 100 °C) |
100-6/°C |
2.4 |
2.5 |
2.9 |
|
Size The size can be made according to customers’ requirement |
mm |
76mm x 115mm x 230mm 64mm x 115mm x 230mm 31mm x 115mm x 230mm |
||
TECHNICAL PROPERTY FOR CARBON BRICK
SPECIFICATION |
UNIT |
Non-impregnated |
Impregnated |
|
Bulk Density |
g/cm3 |
1.5-1.65 |
1.65-1.8 |
|
Porosity |
% |
10to20 |
≤8 |
|
Compressive Strength |
Mpa |
45-65 |
≥80 |
|
Bending Strength |
Mpa |
18 |
≥26 |
|
Tensile Strength |
Mpa |
8 |
≥12.5 |
|
Ash Content |
% |
≤3 |
≤3 |
|
Using Temperature |
℃ |
800-1000 |
≤180 |
|
Acid Resisting |
HCL+H2SO4, 20% |
≥98 |
≥99 |
|
Alkali Resisting |
% |
≥98 |
Nil |
|
SIZE |
240 x 115 x 20mm (Thick: 30mm 40mm 50mm 65mm 80mm 100mm) |
|||
PACKAGE |
Carton on wooden pallet or by negotiation. |
|||
PACKAGE
JX MAIN MARKET ALL OVER THE WORLD
JX PRODUCTION SHOP
JX PROFESSIONAL TEST EQUIPMENTS
Send Inquiry to This Supplier
You May Also Like
-
Jilin Carbon Graphite Electrode Rod UHP HP RP Grade for Steel Mill EAF Furnace Direct Factory SupplyNegotiableMOQ: 50 Tons
-
Graphite FeltNegotiableMOQ: 1
-
Graphite Bush Bearing, Mechanical Bearing, China Bearing FactoryUS$ 0.01 - 3MOQ: 500 Pieces
-
ISO Approval GPC/petroleum Coke/carbon AdditiveUS$ 500 - 700MOQ: 20 Tons
-
Carbon PackingUS$ 10 - 100MOQ: 1 Piece
-
Graphite RotorNegotiableMOQ: 3 Combos
-
Dia 24 Inch Graphite Electrodes Uhp 600X2400 600*2400 2400mm Length Graphite Electrode UHP600US$ 2200 - 2500MOQ: 20 Tons
-
UHP Graphite Electrode for SteelmakingNegotiableMOQ: 10 Tons
-
UHP φ350mm Graphite Electrode, Carbon Electrode, Carbon Rod for Steelmaking, New Energy, High-efficiency, Energy-saving Material, Factory PriceNegotiableMOQ: 10 Tons
-
Carbon Graphite Electrode With Nipples RP HP UHP 750mm 700mm 650mm 600mm 550mm 500mm 450mm 400mmCustomized Dia 800-1400mmUS$ 1200MOQ: 100 Pieces